Product Details:
|
Material: | Tungsten Carbide | Application: | Blank Of Circular Blades |
---|---|---|---|
Hardness: | 91.9HRA | TRS: | 3800 |
Density: | 14.5 | ISO Grade: | K40 |
OD: | 180mm | ID: | 50mm |
Thickness: | 3mm | Parallelism: | 0.05 |
Roughness: | Ra 0.8 | Cutting Angle: | No Degree |
High Light: | Carbide Circular Blades OD 180mm,K40 Carbide Circular Blades |
Carbide Circular Blades Ground Blanks Carbide Slitter Knives For Metal Cutting
OD: 180mm
ID: 150mm
Thickness: 3mm
Parallelism: 0.05
Ra 0.8
Application
Our circular blades are widely used for making saw blades, slitter knives, for cutting metal, no-ferrous materials, plastic, paper and so on.
Dimension of our slitter knives:
OD from 30 to 350mm;
Thickness from 0.6-15mm
Flatness could be 0.005
Concentricity could be 0.005
Precision ground blank or raw sintered blank are avaliable.
Recomented carbide grades for metal working are as follows:
ISO Code | Grade | Binder | Grain size | Density g/cm3 |
Hardness HRA |
TRS N/mm2 |
Application |
K10 | YF06 | 6 | fine | 14.9 | 92 | 2000 | Fine grain size, good wear resistance. Semi-finishing of chilled cast iron, non-ferrous metals, semi-finishing and finishing of hardness steel, alloy steel. |
K20 | YG8 | 8 | medium | 14.7 | 89.5 | 2500 | High stength in use, impact and shock resistance higher than YG6, but wear resistance and cutting speed comparatively lower. Roughing of cast iron, non-ferrous metals and the alloys as wee as non metallic materials at low cutting speed. |
K30 | YS2T | 10 | fine | 14.5 | 92 | 2350 | Fine grain size, high resistance high bending strength, high resistance to bonding, high thermal strength. Machining of refractory alloys, stainless steel and high manganese steel, etc. |
Our advantages:
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
The internal stress can be removed through the cryogenic process to improve the microstructure.
The internal stress can be removed through the vibration process to improve the overall performance.
The service can be improved through the heat treatment process.