Product Details:
|
Material: | Tungsten Carbide | Type: | Carbide Cutter |
---|---|---|---|
Application: | For ALU Or Other Metal | ISO Grade: | K20 |
TRS: | 2800 | Hardness: | HRA 90.5-92.5 |
Density: | 14.5 | Length: | 45 |
Width Dia: | 2 | Thickness: | 2 |
High Light: | 110 Degree Carbide Wear Strips,Carbide Wear Strips K20,Alu tungsten carbide strip |
Carbide Cutter Metal Working Cutter Strip Shearing Blades K20 Alu Knives
Customized carbide cutters for metal working tools
Length 45mm
Width 2mm
Thickness 2mm
Cutting angle 110°
Recommended grades for metal working
Application Code |
Chemical Composition | Physical Properties of powder |
Physical and mechanical properties and mirco structure as stintered |
Application recommended | ||||||||
Co | Tic/ TacNbc |
WC | Hall Flow | Apparent density |
Density | Hardness | Transverse rupture strength |
Coercivity | Magnetic saturation |
Porosity | ||
s/25cm3 | g/cm3 | g/cm3 | HV 30 | N/mm2 | KA/m | % | ||||||
P10 | 9.5 | 35 | 55.5 | 35 | 2.52 | 10.3 | 1525-1675 | ≥1130 | 9.2-11.5 | 8.3-9.5 | A02 B00 | For machining steel and cast steel |
P20 | 8.2 | 14 | 77.8 | 32 | 2.83 | 11.52 | 1560-1700 | ≥1400 | 12.0-15.5 | 7.5-8.2 | A02 B00 | For machining long-chip steel, cast steel and forgeable cast iron |
P25 | 9.5 | 21.9 | 68.6 | 35 | 2.5 | 11.42 | 1400-1550 | ≥1700 | 8.0-10.4 | 8.5-9.5 | A02 B00 | |
P30 | 9.3 | 6.3 | 84.4 | 32 | 3.14 | 13.02 | 1370-1560 | ≥1750 | 9.5-12.5 | 8.6-9.2 | A02 B00 | |
10 | 20 | 70 | 33 | 3.08 | 12.86 | 1425-1575 | ≥1600 | 13.7-15.5 | 8.1-9.1 | A02 B00 | ||
P35 | 11 | 12 | 77 | 35 | 3.24 | 13.12 | 1320-1460 | ≥1650 | 10.7-13.1 | 9.1-10.1 | A02 B00 | For machining steel and cast steel parts with different pores including sand holes. |
P40 | 12 | 18.93 | 69.07 | 35 | 2.88 | 12.75 | ≥1400 | ≥2250 | 15.0-19.0 | 10.0-11.2 | A04 B02 |
Our advantages:
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
The internal stress can be removed through the cryogenic process to improve the microstructure.
The internal stress can be removed through the vibration process to improve the overall performance.
The service can be improved through the heat treatment process.