Product Details:
|
| Material: | Tungsten Carbide | Type: | Slitter Knives |
|---|---|---|---|
| Application: | For Cutting Silicon Steel Sheet | ISO Grade: | K30 |
| TRS: | 2200 | Hardness: | HRA 92 |
| Density: | 14.8 | Diameter: | 30-500 |
| Thickness: | 0.6-20 | ||
| High Light: | Solid Carbide Slitter Blades,Carbide Slitter Blades K30,K30 Solid Carbide Slitter Blades |
||
K30 Solid Carbide Slitter Blades Metal Circular Knives For Cutting Silicon Sttel Sheet
Solid carbide slitter blades are widely used for cutting metal, non-ferrous, plastic, paper and so on.
OED solid carbide circular knives dimension range are as follows:
Diameter 30-500mm, up to 500mm diameter.
Thickness 0.6-20mm, thin blade is available.
Application: for metal working.
Parallelism 0.005
Roundness 0.01
Cutting angle. double angle, single angle, raw sintered blank
Recommended grades for Metal working:
| Application Code |
Chemical Composition | Physical Properties of powder |
Physical and mechanical properties and mirco structure as stintered |
Application recommended | ||||||||
| Co | Tic/ TacNbc |
WC | Hall Flow | Apparent density |
Density | Hardness | Transverse rupture strength |
Coercivity | Magnetic saturation |
Porosity | ||
| s/25cm3 | g/cm3 | g/cm3 | HV 30 | N/mm2 | KA/m | % | ||||||
| K05 | 6 | 0.3 | 93.7 | 35 | 3.45 | 14.94 | 1650-1750 | ≥1560 | 19.5-24.5 | 5.1-5.9 | A02 B02 | For machining super-hard grey cast steel, hardening steel, chilled iron, high silicon-aluminum alloy,high wear-resistant plastic, hard paper plate and ceramics. |
| 6 | 2 | 92 | 35 | 2.85 | 14.95 | 1350-1500 | ≥1600 | 21.5-26.5 | 4.9-5.9 | A02 B02 | ||
| K10-K15 | 6 | 0.4 | 93.6 | 35 | 3.45 | 14.91 | 1665-1835 | ≥123 | 19.5-24.5 | 5.2-6.2 | A02 B02 | For machining cast iron with hardness higher than 200HB, short-chip forgeable cast iron, silicon-aluminum alloy, copper alloy, plastic, glass, ceramics and stones. |
| K20 | 6 | 0.4 | 93.6 | 35 | 3.25 | 14.9 | 1600-1700 | ≥1670 | 16.3-19.2 | 5.2-6.0 | A02 B02 | For machining grey cast iron with hardness lower than 200HB, non-ferrous metal, copper, brass and aluminum |
| 7.8 | 1 | 91.2 | 35 | 3.35 | 14.61 | ≥1400 | ≥2000 | 15.0-18.0 | 6.6-7.8 | A02 B02 | ||
| K30 | 6 | 2 | 92 | 35 | 3.45 | 14.8 | 1450-1600 | ≥1320 | 13.5-15.1 | 5.3-6.0 | A02 B00 | For machining low-hardness grey cast iron, low-strength steel and compact wood. |