Product Details:
|
Material: | Tungsten Carbide | Type: | Carbide Milling Tools |
---|---|---|---|
Application: | For Aluminum Milling | ISO Grade: | K30 |
TRS: | 2600 | Hardness: | HRA 92.5 |
Density: | 14.58 | OD: | 42 |
ID: | 12 | Thickness: | 14 |
Highlight: | K30 Carbide Milling Inserts,Carbide Milling Inserts HRA 92.5,ID 12mm Carbide Milling Inserts |
YG8 Aluminum Milling Inserts K30 Carbide Metal Cutting Tools
Special Alu milling tools. Customized by the customer for milling aluminum material. The milling inserts requests high hardness and wear-resistance performance, and OED recommended K30(YG8) as material for these inserts.
Testing report:
Compare to the previous milling insert 3,000pcs, OED milling tools worked for machining 5,500pcs. The service life has been increased almost 80%.
Main dimension:
OD 42mm
ID 12mm
Thickness 12mm
Ground surface, roughness Ra 0.8
Recommended grades for metalworking
Application Code |
Chemical Composition | Physical Properties of powder |
Physical and mechanical properties and micro structure as sintered |
Application recommended | ||||||||
Co | Tic/ TacNbc |
WC | Hall Flow | Apparent density |
Density | Hardness | Transverse rupture strength |
Coercivity | Magnetic saturation |
Porosity | ||
s/25cm3 | g/cm3 | g/cm3 | HV 30 | N/mm2 | KA/m | % | ||||||
P10 | 9.5 | 35 | 55.5 | 35 | 2.52 | 10.3 | 1525-1675 | ≥1130 | 9.2-11.5 | 8.3-9.5 | A02 B00 | For machining steel and cast steel |
P20 | 8.2 | 14 | 77.8 | 32 | 2.83 | 11.52 | 1560-1700 | ≥1400 | 12.0-15.5 | 7.5-8.2 | A02 B00 | For machining long-chip steel, cast steel and forgeable cast iron |
P25 | 9.5 | 21.9 | 68.6 | 35 | 2.5 | 11.42 | 1400-1550 | ≥1700 | 8.0-10.4 | 8.5-9.5 | A02 B00 | |
P30 | 9.3 | 6.3 | 84.4 | 32 | 3.14 | 13.02 | 1370-1560 | ≥1750 | 9.5-12.5 | 8.6-9.2 | A02 B00 | |
10 | 20 | 70 | 33 | 3.08 | 12.86 | 1425-1575 | ≥1600 | 13.7-15.5 | 8.1-9.1 | A02 B00 | ||
P35 | 11 | 12 | 77 | 35 | 3.24 | 13.12 | 1320-1460 | ≥1650 | 10.7-13.1 | 9.1-10.1 | A02 B00 | For machining steel and cast steel parts with different pores including sand holes. |
P40 | 12 | 18.93 | 69.07 | 35 | 2.88 | 12.75 | ≥1400 | ≥2250 | 15.0-19.0 | 10.0-11.2 | A04 B02 |
Our advantages:
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
The internal stress can be removed through the cryogenic process to improve the microstructure.
The internal stress can be removed through the vibration process to improve the overall performance.
The service can be improved through the heat treatment process.
Why choose us for carbide wear parts: