Material: | Tungsten Carbide | Application: | Ceramic Wear Parts |
---|---|---|---|
ISO Grade: | Ceramic | Hardness: | HV30 1300 |
TRS: | 3300 | Density: | 14.2 |
Tolerance: | ISO 2768 M | ||
High Light: | OED Ceramic Wear Parts,ISO 2768 M Ceramic Wear Parts,3300 TRS Ceramic Shaft Sleeve |
Ceramic Pad Printer Rings Piston Wear Sleeves Carbide Wear Parts
Ceramic offer better heat and wear resistance than carbide and can be harder. Therefore, in many low impact requirements of the use of environment, ceramic can be very good use in different applications.
Our products range of customized wear parts:
Why choose us for carbide wear parts:
Recommended carbide grades for wear parts:
Application Code |
Grade | Chemical Composition | Physical and mechanical properties and mirco structure as stintered |
Application recommended | |||||||
Co | Tic/ TacNbc |
WC | Density | Hardness | Hardness | TRS | Coercivity | Grain Size | |||
g/cm3 | HV 30 | HRA | N/mm2 | KA/m | μm | ||||||
G05 | OG6X | 6 | 94 | 14.85~15.05 | ≥1500 | ≥91.00 | ≥1700 | 19.2~25.7 | 0.8 | For drilling soft or medium hard rock formation with a single-zxis compression strength less than 60 Mpa | |
G10 | OG6 | 6 | 94 | 14.85~15.05 | ≥1350 | ≥89.50 | ≥1800 | 12.0~15.9 | 1.6 | ||
G15 | OG8C | 8 | 92 | 14.55~14.75 | ≥1150 | ≥87.50 | ≥2000 | 7.6~9.6 | 2.5 | For drilling soft or medium hard rock formation with a single-zxis compression strength of60-120 Mpa | |
G20 | OG11C | 12 | 88 | 14.20~14.40 | ≥1050 | ≥86.50 | ≥2400 | 6.0~8.0 | 2.0 | ||
G30 | OG15 | 15 | 85 | 13.95~14.15 | ≥1050 | ≥86.50 | ≥2220 | 8.0~10.8 | 1.6 | For drilling soft or medium hard rock formation with a single-zxis compression strength of 120-200 Mpa | |
G40 | OG20 | 20 | 80 | 13.45~13.65 | ≥750 | ≥83.50 | ≥2480 | 7.0~8.9 | 1.0 | ||
G50 | OG25 | 25 | 75 | 13~13.15 | ≥650 | 82.5 | ≥3500 | 10~13 | 1.6 | For drilling soft or medium hard rock formation with a single-zxis compression strength of 120-200 Mpa |