Product Details:
|
| Material: | Tungsten Carbide | Application: | Carbide Rings |
|---|---|---|---|
| ISO Grade: | K40 | Hardness: | HV30 1500 |
| TRS: | 3800 | Density: | 14.45 |
| Tolerance: | ISO 2768 F | ||
| High Light: | Ceramic Wear Parts Ra 0.8,12mm Ceramic Wear Parts |
||
Finished Ground Carbide Wear Ring With Steps Wear Parts For Machanical Parts
OD 42mm
ID 38mm
Height 12mm
Roughness Ra 0.8
Remove all sharp edges
Why choose us for carbide wear parts:
Our products range of customized wear parts:
Recommended carbide grades for wear parts:
| Application Code |
Grade | Chemical Composition | Physical and mechanical properties and mirco structure as stintered |
Application recommended | |||||||
| Co | Tic/ TacNbc |
WC | Density | Hardness | Hardness | TRS | Coercivity | Grain Size | |||
| g/cm3 | HV 30 | HRA | N/mm2 | KA/m | μm | ||||||
| G05 | OG6X | 6 | 94 | 14.85～15.05 | ≥1500 | ≥91.00 | ≥1700 | 19.2～25.7 | 0.8 | For drilling soft or medium hard rock formation with a single-zxis compression strength less than 60 Mpa | |
| G10 | OG6 | 6 | 94 | 14.85～15.05 | ≥1350 | ≥89.50 | ≥1800 | 12.0～15.9 | 1.6 | ||
| G15 | OG8C | 8 | 92 | 14.55～14.75 | ≥1150 | ≥87.50 | ≥2000 | 7.6～9.6 | 2.5 | For drilling soft or medium hard rock formation with a single-zxis compression strength of60-120 Mpa | |
| G20 | OG11C | 12 | 88 | 14.20～14.40 | ≥1050 | ≥86.50 | ≥2400 | 6.0～8.0 | 2.0 | ||
| G30 | OG15 | 15 | 85 | 13.95～14.15 | ≥1050 | ≥86.50 | ≥2220 | 8.0～10.8 | 1.6 | For drilling soft or medium hard rock formation with a single-zxis compression strength of 120-200 Mpa | |
| G40 | OG20 | 20 | 80 | 13.45～13.65 | ≥750 | ≥83.50 | ≥2480 | 7.0～8.9 | 1.0 | ||
| G50 | OG25 | 25 | 75 | 13~13.15 | ≥650 | 82.5 | ≥3500 | 10~13 | 1.6 | For drilling soft or medium hard rock formation with a single-zxis compression strength of 120-200 Mpa | |