Product Details:
|
Material: | Tungsten Carbide | Application: | Carbide Rods |
---|---|---|---|
ISO Grade: | K30/K40 | Cobalt: | 9% |
Hardness: | HRA 93.5 | TRS: | 3800 |
Density: | 14.45 | Grain Size: | Nano |
Length: | 79mm | OD: | OD12mm H6 |
High Light: | 9% Cobalt Tungsten Carbide Rods,Finished Ground Tungsten Carbide Rods,Alluminum Machining Ground Carbide Rod |
Finished Ground 12% Cobalt Tungsten Carbide Rods For Aluminum Machining
Specification:
ISO grade K40
Diameter: 16mm h6 tolerance -0.011mm
Length 80mm +0.5mm
Grain size: 0.3μm
Density: 14.4
Extremely high wear resistance and strength, suitable for high-hard materials (HRC55 and above) finishing, 316L stainless steel, high-gloss surface treatment of aluminum alloy, titanium alloy, stainless steel, high-temperature alloy, and other difficult-to-machine materials (composite wood).
OED Carbide grades for Rods
OEDF06 | OEDU06 | OEDU08E | OED10A | OED10.2 | OED10D | OEDU12 | ||
ISO range | K05-K10 | K05-K10 | K05-K10 | K20-K30 | K20-K30 | K30-K40 | K30-K40 | |
WC+other | % | 93.7 | 93 | 92 | 91 | 89.4 | 86.5 | 86.5 |
Co | % | 6 | 6 | 8 | 8 | 10 | 12 | 12 |
WC grain size | μm | 0.6 | 0.4 | 0.4 | 0.8 | 0.6 | 0.6 | 0.4 |
density | g/㎝³ | 14.9 | 14.75 | 14.62 | 14.65 | 14.42 | 14.15 | 14.05 |
hardness | Hv30 | 1850 | 1890 | 1850 | 1700 | 1620 | 1700 | 1750 |
HRA | 93.5 | 93.8 | 93.5 | 92.5 | 92.2 | 92.5 | 92.8 | |
transverse rupture strength | N/mm² | 3800 | 3000 | 4000 | 3000 | 4200 | 4000 | 4200 |
Metallograph |
Grade recommendation.
Non-coated Grade | Application | |||||||
6% Co | Reamer, for machining grey cast iron nonferrous metal, hardening steel, chilled iron, with high wear resistance. | |||||||
8% Co | Drills and taps, for machining grey cast iron, nonferrous metal, with good wear resistance. | |||||||
10% Co | It's widely used for milling tools, good performance of wearability bending strength, and toughness. | |||||||
12% Co | High-speed milling tools, for machining steel and high silicon-aluminum alloy, with perfect wear resistance, bending strength, and toughness. | |||||||
The other grades are available. Please let us know the usage and workpiece, then we can recommend the most suitable grade for you. |
Our advantages:
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
The internal stress can be removed through the cryogenic process to improve the microstructure.
The internal stress can be removed through the vibration process to improve the overall performance.
The service can be improved through the heat treatment process.
CIP forming.
CIP Forming can eliminate the internal defects of raw sintered carbide blanks in particular. It can provide uniform density suppression products for the thick carbide strips/plate and special shape carbide products.
Why choose us for carbide wear parts: