Product Details:
|
| Material: | Tungsten Carbide | Application: | Carbide Wheel |
|---|---|---|---|
| ISO Grade: | G10 | Hardness: | HV30 1500 |
| TRS: | 2800 | Density: | 14.8 |
| Tolerance: | ISO 2768 M | ||
| High Light: | Sintered Tungsten Carbide Wheel,Tungsten Carbide Wheel Special,G10 tungsten carbide disc |
||
Raw Sintered Carbide Wheel Special Carbide Wear Parts
Compared with traditional silicon carbide, carbide has more stable chemical properties, such as good wear resistance, high thermal conductivity, low coefficient of friction, small coefficient of expansion, acid resistance, alkali resistance, self-lubrication, corrosion resistance, high thermal conductivity and small expansion coefficient, making it an ideal material for mechanical wear-resistant parts.
Recommended carbide grades for wear parts:
| Application Code |
Grade | Chemical Composition | Physical and mechanical properties and mirco structure as stintered |
Application recommended | |||||||
| Co | Tic/ TacNbc |
WC | Density | Hardness | Hardness | TRS | Coercivity | Grain Size | |||
| g/cm3 | HV 30 | HRA | N/mm2 | KA/m | μm | ||||||
| G05 | OG6X | 6 | 94 | 14.85～15.05 | ≥1500 | ≥91.00 | ≥1700 | 19.2～25.7 | 0.8 | For drilling soft or medium hard rock formation with a single-zxis compression strength less than 60 Mpa | |
| G10 | OG6 | 6 | 94 | 14.85～15.05 | ≥1350 | ≥89.50 | ≥1800 | 12.0～15.9 | 1.6 | ||
| G15 | OG8C | 8 | 92 | 14.55～14.75 | ≥1150 | ≥87.50 | ≥2000 | 7.6～9.6 | 2.5 | For drilling soft or medium hard rock formation with a single-zxis compression strength of60-120 Mpa | |
| G20 | OG11C | 12 | 88 | 14.20～14.40 | ≥1050 | ≥86.50 | ≥2400 | 6.0～8.0 | 2.0 | ||
| G30 | OG15 | 15 | 85 | 13.95～14.15 | ≥1050 | ≥86.50 | ≥2220 | 8.0～10.8 | 1.6 | For drilling soft or medium hard rock formation with a single-zxis compression strength of 120-200 Mpa | |
| G40 | OG20 | 20 | 80 | 13.45～13.65 | ≥750 | ≥83.50 | ≥2480 | 7.0～8.9 | 1.0 | ||
| G50 | OG25 | 25 | 75 | 13~13.15 | ≥650 | 82.5 | ≥3500 | 10~13 | 1.6 | For drilling soft or medium hard rock formation with a single-zxis compression strength of 120-200 Mpa | |
Our products range of customized wear parts:
Why choose us for carbide wear parts: